| Customization: | Available |
|---|---|
| Environmental Protection: | No |
| Color: | Yellow |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
The EPDM-g-MAH Aging Resistance A state-of-the-art product that provides remarkable performance in strengthening the aging resistance and cold resistance capabilities of EPDM and nylon materials is called Cold Resistance Super Tough Nylon Toughening Compatibilizer. This compatibilizer is made particularly to increase the compatibility between nylon and EPDM, creating a material that is robust, long-lasting, and better able to withstand aging and low temperatures. This product is redefining the market with its distinctive formulation and cutting-edge technology by offering improved performance and dependability across a range of applications.
Enhancing the age resistance and cold resistance capabilities of EPDM and nylon materials is the main goal of the age Resistance EPDM-g-MAH Cold Resistance Super Tough Nylon Toughening Compatibilizer. By serving as a link between the two components, this compatibilizer increases their compatibility and produces a synergistic result. It successfully stops EPDM and nylon from deteriorating from age and exposure to cold temperatures, assuring the life and durability of the finished product. This compatibilizer also improves the material's strength and toughness, making it ideal for demanding applications.
| Test item | Test data | Test method |
| density | 0.87 g/cm³ | ASTM D792 ISO 1183 |
| Melt index | 0.1-0.4(190ºC,2.16kg)g/10min | ASTM D1238 ISO 1133 |
| Grafting | High | rateacid-base titration |