| Customization: | Available |
|---|---|
| Certification: | REACH |
| Environmental Protection: | No |
|
Still deciding? Get samples of $ !
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
SEBS is often added to the blending system as a compatibilizer and toughening agent. In order to increase the blending compatibility with the polymer and reduce the interfacial tension, it is necessary to carry out grafting solution modification or blending solution modification on SEBS.
The most common SEBS modification method is to graft it with maleic anhydride (MAH) to increase the molecular polarity, making it compatible with some polymers.
such as polyamide (PA)] compatibility, many research results show that SEBS-g-MAH is a good reactive compatibilization of PPO/PA66 blends, which effectively improves the interaction between the PPO/PA66 phase interface force, making the dispersed phase in the base particles smaller and uniform, becoming a stable sub-microscopic dispersion state. The addition of SEBS… gMAH has a good effect on the tensile strength, flexural strength and Izod notched impact strength of PPO/PA66 alloy. There is an improvement, but the rigidity and heat resistance are slightly reduced, and the cost of the alloy is greatly increased; therefore, the use of 5~10 parts of SEBS-g-MAH can obtain a PPO/PA66 alloy with excellent comprehensive properties. With SEBS-g-MAH - With the addition of g- -MAH, the glass transition temperature of PA66 in the blend system increases, and the glass transition temperature of PPO decreases, whether PPO is the continuous phase or PA66 is the continuous phase, and SEBS- g- - As the MAH increases, the greater the change in glass transition temperature.
| Appearance | granules |
| Color | White or light yellow |
| Melt index(190ºC, 5 kg): g/10min | 1-6g |
| Maleic Anhydride Content | High |
| Density(g/cm3) | 0.94-0.96 |
Notes[1]LOW<0.4wt%; Middle(0.4-0.8wt%); High(0.81-1.2wt%);U high(1.21-3wt%).
Coace® W1G-5 is a maleic anhydride grafted polymer with SEBS elastomer as the base material. It has good stability and aging resistance and has the appearance of white or light yellow particles.
Using maleic anhydride grafted polymer and SEBS elastomer as its foundation material, the Ageing Resistance PC/ABS Alloy Toughener is a significant advancement in the field of polymer modification technology. Its one-of-a-kind composition improves the durability, impact resistance, and ageing resistance of PC/ABS alloys, which makes it an excellent option for a wide variety of applications. Whether it is utilised in the automotive industry, the electronics industry, the consumer goods industry, or the industrial sector, this toughener provides exceptional performance and reliability. When it comes to the production of high-quality, long-lasting products, manufacturers can reap the benefits of its adaptability, superior mechanical qualities, and outstanding resistance to the effects of ageing. For all of your polymer alloy requirements, the Ageing Resistance PC/ABS Alloy Toughener presents you with the opportunity to embrace endurance and longevity.